{"id":38483,"date":"2024-06-05T18:03:38","date_gmt":"2024-06-05T16:03:38","guid":{"rendered":"https:\/\/ssef.ch\/?p=38483"},"modified":"2024-06-10T17:33:43","modified_gmt":"2024-06-10T15:33:43","slug":"a-descriptive-study-on-as-grown-and-hpht-treated-cvd-synthetic-diamonds","status":"publish","type":"post","link":"https:\/\/www.ssef.ch\/de\/a-descriptive-study-on-as-grown-and-hpht-treated-cvd-synthetic-diamonds\/","title":{"rendered":"A descriptive study on as-grown and HPHT-treated CVD synthetic diamonds"},"content":{"rendered":"\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

By Dr. M. Mintrone, first published in Facette 29<\/a> (May 2024)<\/strong><\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/div>\n\t\t\t\t\t<\/div>\n\t\t<\/section>\n\t\t\t\t

\n\t\t\t\t\t\t
\n\t\t\t\t\t
\n\t\t\t
\n\t\t\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\tThe Swiss Gemmological Institute is testing more than one million colourless melee diamonds for the Swiss watch and jewellery industry on an annual basis to guarantee that no synthetic diamonds are mixed within natural melee diamond batches. Therefore, it remains crucial for our institute to be at the vanguard of the knowledge concerning recent CVD and HPHT synthetic production and to invest resources and time in diamond research.\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t\t\t\t
\n\t\t\t\t\t\t\t\t\t\t\"\"\t\t\t\t\t\t\t\t\t\t\t
Figure 1: Fluorescence colours observed in CVD diamonds with the DiamondViewTM. (a) and (b) reddish-orange and yellow fluorescence respectively, probably related to NV centres. (c) and (d) purplish-pink and blue fluorescence respectively, generally attributed to dislocations. (e) and (f) green and greenish-blue fluorescence respectively, generally typical of HPHT treated CVD, the green fluorescence is attributed to a H3 centre. Image: SSEF.<\/figcaption>\n\t\t\t\t\t\t\t\t\t\t<\/figure>\n\t\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

In a recent research project with Armin Spelina, a student of the University Basel, we investigated 20 synthetic diamonds (CVD) from a private donation with diameters between 0.9 and 1.2 mm. FTIR analyses showed that all the tested CVD samples are type IIa (i.e. no detectable nitrogen), which – to our knowledge and based on literature \u2013 is always the case for colourless CVD synthetic diamonds (Eaton-Magana et al., 2020). Under UV-lamp excitation, 19 of these CVDs display fluorescence colours that are rarely observed in natural diamonds (Fig. 1a, b, c, e, and f). The most observed fluorescence colours were green and greenish-blue. However, one CVD (Fig. 1d) exhibits a blue fluorescence, similar to the reaction commonly observed in natural diamonds. Due to the small size of the samples, typical CVD growth structures like striations were only visible in a few samples (Fig. 1f).<\/p>\n

Photoluminescence (PL) analyses at low temperature (-196\u00b0C) showed that 8 of these synthetic CVDs were as-grown and 12 HPHT treated. The SiV defect (737 nm) was detected in all the investigated samples, which is a typical feature of CVD synthetic diamonds (Fig. 2a). As-grown synthetic CVD always displayed the 467 nm defect, and most showed the 596\/597 nm centre, which is only present in CVD (Fig. 2a and b). As-grown synthetic CVD corresponds to the samples with red, reddish- orange, yellow, purplish-pink, and blue fluorescence colours.<\/p>\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t

\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t\t\t\t
\n\t\t\t\t\t\t\t\t\t\t\"\"\t\t\t\t\t\t\t\t\t\t\t
Figure 2: PL spectra collected at liquid nitrogen temperature (-196\u00b0C) for an as-grown synthetic CVD and an HPHT-treated CVD synthetic diamond. The spectra are shifted vertically for clarity. DRP corresponds to the Diamond Raman Peak. Figure: M. Mintrone, SSEF.<\/figcaption>\n\t\t\t\t\t\t\t\t\t\t<\/figure>\n\t\t\t\t\t\t\t\t\t<\/div>\n\t\t\t\t<\/div>\n\t\t\t\t
\n\t\t\t\t
\n\t\t\t\t\t\t\t\t\t

In contrast, the 12 CVD samples displaying a green or greenish-blue fluorescence showed indications of HPHT treatment. HPHT treatments on CVD synthetic diamonds are generally performed to reduce their initial brownish coloration (Eaton-Magana et al., 2016). This is supported by the absence of the 467 nm centre (correlated with the brownish coloration, Zaitsez et al., 2021). Moreover, the absence of the 596\/597 nm centre and the presence of aggregated nitrogen such as N3, H3, and H4 centres are strong evidence of HPHT treatment. Those CVD synthetic diamonds are also characterized by the presence of numerous peaks between 430-500 nm (Fig. 2a) and 520-580 nm (Fig. 2b) which is common in this type of CVD (Wang et al., 2012).<\/p>

To summarize:<\/p>